New coating systems by AHC Oberflächentechnik protects aluminium-cast alloys from corrosion
Combination coating of hard anodic oxidation plus PFA and a PFA double layer marketed under the name GLISS-COAT®
Hard anodic oxidation has been an established corrosion and wear protection for aluminium alloys for decades. AHC Oberflächentechnik offers this process under the trademark name HART-COAT®. The layer is formed by anodic oxidation in a cooled acid-electrolytic solution, in which the surface of the base aluminium material is converted into aluminium oxide. In this process, the oxide layer uniformly increases inwardly and outwardly, resulting in a defined dimensional change of the component. The excellent atomic bonding to the base material from which the layer is originated is of particular interest here.
PFA (perfluoralkoxyalcane) is a co-polymer made of two thermoplastic polymers and an advancement of the common PTFE (polytetrafluoroethylene). The continuous operating temperature is 260 °C and PFA possesses outstanding properties of chemical resistance. For these reasons, PFA finds typical application as a construction material in chemical apparatus engineering (e.g. heat exchange linings and housing linings). As opposed to PTFE, PFA can be processed thermoplastically. Thanks to the high fluidity of the molten mass, the plastic can be applied and spread homogeneously on surfaces in an injection process.
The novel aspect is the combination of a HART-COAT® layer and a PFA layer (Figure 1) and a so-called PFA double coat (Figure 2).
A suitable pre-treatment and process control ensure excellent bonding of the PFA to the HART-COAT® layer (Figure 1). The porous structure of the HART-COAT® undercoat offers the PFA topcoat an outstanding adherent surface, as well as a distinct and mechanically sustainable foundation for corresponding load profiles. The PFA double coat (Figure 2) bonds very well to the mechanically pre-treated base material and is also well interwoven. A dividing line between the two PFA layers can no longer be identified on the micrograph. The coating is therefore compact and overlapping.
Many kinds of aluminium components coated in this way were subjected to corrosion tests according to VDA 230-214. This standard by the automobile association VDA (Verband der Automobilindustrie e.V.) regulates the resistance test of metallic materials to condensate corrosion in exhaust components. The materials were tested for resistance by subjection to a synthetic condensate K 1.1 (PFA-PFA layer) and K 1.2 (HART-COAT®-PFA layer) and alternating with a thermal load at 200 °C, in which the samples were weathered in an oven one time per week for five hours. The test alternated in cycles of one day and one week:
- Temperature load: 200°C / weekly for 5h and documentation
- Alternating corrosion load 6 days per week with cyclic repeating phases:
- Partial dipping: 6h / daily
- Drying: 2h at approx. 90 °C / daily
- Steam phase: 16h / daily
During the test, the condensate temperature was 50 °C. The pH value of the condensate was checked daily to ensure that there were no changes in the composition of condensate, and the test medium was changed weekly.
The following table shows the compositions of the test condensate.
The entire test duration under aggressive conditions was an amazing six (!) weeks. Those are test conditions that not even stainless steel can withstand undamaged.
There was no attack of any kind of corrosion on the smooth surfaces of the PFA-PFA coated components after the test with the condensate K 1.1. Small bubbles formed at the front sides and at places that appeared somewhat rough. However, these locations are generally not functional surfaces and are covered or overlaid by other components. The outstanding corrosion resistance of the PFA-PFA double coat also proved itself in the Kesternichtest according to DIN EN ISO 6988. There was no visible corrosion on the inner and outer surfaces of the components after 4 cycles (0.2 l SO2) (quality degree Rp10 = no flaws).
The HART-COAT®-PFA coated components displayed similarly positive results after the six-week test with the test condensate. At the end of the test, there were only a few pores found on the smooth surfaces. A somewhat stronger corrosion attack occurred on the non-functional surfaces, e.g. in drilled holes. There was no detected corrosion on the smooth surfaces following 453 hours of the neutral salt spray test according to DIN EN ISO 9227. There were only a few small points detected in the drilled holes and on the edges. Assessment: Rp 9 (flawed surface in %: 0< A 0.1).
Conclusion: The coating systems HART-COAT®-PFA (GLISS-COAT® 2001- F-083) and PFA-PFA (GLISS-COAT® F495) are two processes for coating aluminium-cast parts to withstand the intense attack of acid in the form of steam and liquids over a sufficiently long period of time. They are therefore appropriate for example in coating exhaust components in automotive engines to protect from corrosion inside the engine itself. Furthermore, general applications are available for aluminium-cast parts in sectors where acidic condensation is found at application temperatures exceeding 200 °C: heating systems, air conditioning units, exhaust systems, steam pumps and traps etc. Figure 3 shows that the coating systems possess very good hydrophobic properties as well.
About AHC Oberflächentechnik GmbH
AHC Oberflächentechnik GmbH comprises 15 sites with headquarters in Kerpen, near Cologne. The business of the AHC Group is focused on providing functional coating of technical surfaces as a service. Components e.g. for the automotive industry, the mechanical engineering market or for electricals and electronics are protected against corrosion and wear or given special properties by using patented and in-house-developed processes. Well established processes are hard anodising (HART-COAT®) and Electroless Nickel plating (DURNI-COAT®). With the first process, a hard oxide layer is produced on aluminium-based materials, whereas with the second process, a nickel-phosphorus alloy of specific composition is deposited on ferrous and non-ferrous materials.
Further coatings are suited for magnesium (MAGOXID-COAT®) or titanium materials (KEPLA-COAT®), serve as dry lubricant anti-friction coatings (GLISS-COAT®) or are used in case of loads by friction and vibration corrosion (DURALLOY®).
For patented coatings, licenses are granted all over the world. Worldwide, together with RIAG Oberflächentechnik AG, we cover all the needs for process chemicals for electroless and electrochemical processes for the treatment of metals and plastics.
Research and development are of great importance to the AHC group. Existing processes and applications are optimised and new opportunities are constantly being developed.
AHC consultants support their customers throughout the planning and design stages, assisting them in defining precisely the specification of their requirements as well as selecting the most suitable materials and processes.